株式会社YOOコーポレーション

The surface coated with ECOKIMERA (R) C is not easily stained by effect of antistatics with ionic conductivity.Even if it were stained, can be wiped out by wiping cloth or washed off by water.

Features of ECOKIMERA (R)

Condensate film of inorganic acid origomer composed with phosphoric acid, titanium

Amorphous Inorganic film fomed.

No color, transparent, high hardness(Pensil hardness over 9H), ion conductive

Contact angle of water is 2-20, High hydrophilic.

Stain-proofing, anti-clouding, antistatic, excellent durability.

Low cost, Film fomed at room temerature applicable by air-spray coating as aqueous solution or alcoholic solution

Deodorizing, Anti-bacteria, Fire-proofing, anti-blazing, Fungus-proofing, Weed-proofing, Anti-shell etc.

Recommended application fields of ECOKIMERA (R)

Stain-proofing on glass surface?
Building wall. Window. Salting air protection anti-dulling

..Car. train. bus. Highway

..Architechtural materials. Building wall Concrete cement

..Air conditioner, Bath room, Swimming pool, Hospital

Date / Nov.14 -Nov.18, 2002 Test Sample
SUBSTRATES : Glass plate (100x100mm, t=5)
1.ECOKIMERA(R) C
2. Photo Catalyst
Test Method
[Creation time of Hydrophilic]
After the test sample is washed by pure water and dried for 24 hrs, contact angle is measured at
0,3,6... 24 hrs, under irradiation of BLB,
[Keeping time of Hydrophilic]
Hydrophilic sample of contact angle below 5゜ put in dark room is measured each contact angle at
0,3,6... 24hrs
Test results
Creation time of Hydrophilic Keeping time of Hydrophilic
Times(hrs) 0 3 6 12 24
EKOKIMERA(R) 3.7 3.4 3.1 4.6 4.2
Photo catalyst 80.0 43.1 10.6 5.6 2.0
Times(hrs) 0 3 6 12 24 48
EKOKIMERA(R) 3.7 3.4 3.1 4.6 4.2 8.3
Photo catalyst 80.0 43.1 10.6 5.6 2.0 22.1

SEM Picture

Fact of application

  ECOKIMERA(R) Ray active catalyst
Irradiation of UV Notnecessary Necessary
Organic binder Need not Necessary
Adherency Strong Weak
Transparency Non-colored transparent Whity dull
Durability High durability Detariorate binder and substrates
Applying technic Easy(spraying, dipping, brushing) Required experienced operator
Stocking Stability Stable Difficult for long term
Producton and modifying cost Cheap Expensive
Mechanism of activation Not determined Activated by irradiation of ray